Aqueous lithium-air batteries with a lithium-ion conducting solid electrolyte Li<ce:inf loc="post">1.3</ce:inf>Al<ce:inf loc="post">0.5</ce:inf>Nb<ce:inf loc="post">0.2</ce:inf>Ti<ce:inf loc="post">1.3</ce:inf>(PO<ce:inf loc="post">4</ce:inf>)<ce:inf loc="post">3</ce:inf>

A rechargeable aqueous lithium-air battery with a water-stable high lithium-ion conductivity and an excellent bending strength solid electrolyte as a separator between the lithium metal anode and aqueous electrolyte was developed. The cell consists of a lithium metal anode, a buffer layer of 4 M lit...
Ausführliche Beschreibung

A rechargeable aqueous lithium-air battery with a water-stable high lithium-ion conductivity and an excellent bending strength solid electrolyte as a separator between the lithium metal anode and aqueous electrolyte was developed. The cell consists of a lithium metal anode, a buffer layer of 4 M lithium bis(fluorosulfonyl)imide in ethylene glycol dimethyl ether, a lithium-ion conducting solid electrolyte separator of Li1.3Al0.5Nb0.2Ti1.3(PO4)3 (LANTP), a 10 M LiCl aqueous solution with 1.5 M LiOH, and an activated MnO2 air electrode. The tape-cast water-impermeable LANTP film with a small amount of epoxy resin was used as the separator between the lithium anode and aqueous electrolyte. The conductivity and 3-point bending strength of the ca 0.2 mm thick film was 9.1 × 10−4 S cm−1 at 25 °C and 100 MPa, respectively. The cell with the LANTP film was operated successfully at 0.26 mA cm−2 for more than 30 cycles at room temperature in air. Ausführliche Beschreibung