The use of chitin as a new absorbable suture material—An experimental study
Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3...
Ausführliche Beschreibung
Autor*in: |
---|
Format: |
E-Artikel |
---|---|
Sprache: |
Englisch |
Erschienen: |
1988 |
---|
Umfang: |
7 |
---|
Reproduktion: |
Springer Online Journal Archives 1860-2002 |
---|---|
Übergeordnetes Werk: |
in: Surgery today - 1971, 18(1988) vom: Mai, Seite 533-539 |
Übergeordnetes Werk: |
volume:18 ; year:1988 ; month:05 ; pages:533-539 ; extent:7 |
Links: |
---|
Katalog-ID: |
NLEJ20764215X |
---|
LEADER | 01000caa a22002652 4500 | ||
---|---|---|---|
001 | NLEJ20764215X | ||
003 | DE-627 | ||
005 | 20210706233604.0 | ||
007 | cr uuu---uuuuu | ||
008 | 070528s1988 xx |||||o 00| ||eng c | ||
035 | |a (DE-627)NLEJ20764215X | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
245 | 1 | 0 | |a The use of chitin as a new absorbable suture material—An experimental study |
264 | 1 | |c 1988 | |
300 | |a 7 | ||
336 | |a nicht spezifiziert |b zzz |2 rdacontent | ||
337 | |a nicht spezifiziert |b z |2 rdamedia | ||
338 | |a nicht spezifiziert |b zu |2 rdacarrier | ||
520 | |a Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. | ||
533 | |f Springer Online Journal Archives 1860-2002 | ||
700 | 1 | |a Tachibana, Mitsuo |4 oth | |
700 | 1 | |a Yaita, Akira |4 oth | |
700 | 1 | |a Taniura, Hiroyuki |4 oth | |
700 | 1 | |a Fukasawa, Kimiaki |4 oth | |
700 | 1 | |a Nagasue, Naofumi |4 oth | |
700 | 1 | |a Nakamura, Teruhisa |4 oth | |
773 | 0 | 8 | |i in |t Surgery today |d 1971 |g 18(1988) vom: Mai, Seite 533-539 |w (DE-627)NLEJ188991352 |w (DE-600)1463169-6 |x 1436-2813 |7 nnns |
773 | 1 | 8 | |g volume:18 |g year:1988 |g month:05 |g pages:533-539 |g extent:7 |
856 | 4 | 0 | |u http://dx.doi.org/10.1007/BF02471487 |
912 | |a GBV_USEFLAG_U | ||
912 | |a ZDB-1-SOJ | ||
912 | |a GBV_NL_ARTICLE | ||
951 | |a AR | ||
952 | |d 18 |j 1988 |c 5 |h 533-539 |g 7 |
matchkey_str |
article:14362813:1988----::huefhtnsnwbobbeuueaeil |
---|---|
hierarchy_sort_str |
1988 |
publishDate |
1988 |
allfields |
(DE-627)NLEJ20764215X DE-627 ger DE-627 rakwb eng The use of chitin as a new absorbable suture material—An experimental study 1988 7 nicht spezifiziert zzz rdacontent nicht spezifiziert z rdamedia nicht spezifiziert zu rdacarrier Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. Springer Online Journal Archives 1860-2002 Tachibana, Mitsuo oth Yaita, Akira oth Taniura, Hiroyuki oth Fukasawa, Kimiaki oth Nagasue, Naofumi oth Nakamura, Teruhisa oth in Surgery today 1971 18(1988) vom: Mai, Seite 533-539 (DE-627)NLEJ188991352 (DE-600)1463169-6 1436-2813 nnns volume:18 year:1988 month:05 pages:533-539 extent:7 http://dx.doi.org/10.1007/BF02471487 GBV_USEFLAG_U ZDB-1-SOJ GBV_NL_ARTICLE AR 18 1988 5 533-539 7 |
spelling |
(DE-627)NLEJ20764215X DE-627 ger DE-627 rakwb eng The use of chitin as a new absorbable suture material—An experimental study 1988 7 nicht spezifiziert zzz rdacontent nicht spezifiziert z rdamedia nicht spezifiziert zu rdacarrier Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. Springer Online Journal Archives 1860-2002 Tachibana, Mitsuo oth Yaita, Akira oth Taniura, Hiroyuki oth Fukasawa, Kimiaki oth Nagasue, Naofumi oth Nakamura, Teruhisa oth in Surgery today 1971 18(1988) vom: Mai, Seite 533-539 (DE-627)NLEJ188991352 (DE-600)1463169-6 1436-2813 nnns volume:18 year:1988 month:05 pages:533-539 extent:7 http://dx.doi.org/10.1007/BF02471487 GBV_USEFLAG_U ZDB-1-SOJ GBV_NL_ARTICLE AR 18 1988 5 533-539 7 |
allfields_unstemmed |
(DE-627)NLEJ20764215X DE-627 ger DE-627 rakwb eng The use of chitin as a new absorbable suture material—An experimental study 1988 7 nicht spezifiziert zzz rdacontent nicht spezifiziert z rdamedia nicht spezifiziert zu rdacarrier Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. Springer Online Journal Archives 1860-2002 Tachibana, Mitsuo oth Yaita, Akira oth Taniura, Hiroyuki oth Fukasawa, Kimiaki oth Nagasue, Naofumi oth Nakamura, Teruhisa oth in Surgery today 1971 18(1988) vom: Mai, Seite 533-539 (DE-627)NLEJ188991352 (DE-600)1463169-6 1436-2813 nnns volume:18 year:1988 month:05 pages:533-539 extent:7 http://dx.doi.org/10.1007/BF02471487 GBV_USEFLAG_U ZDB-1-SOJ GBV_NL_ARTICLE AR 18 1988 5 533-539 7 |
allfieldsGer |
(DE-627)NLEJ20764215X DE-627 ger DE-627 rakwb eng The use of chitin as a new absorbable suture material—An experimental study 1988 7 nicht spezifiziert zzz rdacontent nicht spezifiziert z rdamedia nicht spezifiziert zu rdacarrier Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. Springer Online Journal Archives 1860-2002 Tachibana, Mitsuo oth Yaita, Akira oth Taniura, Hiroyuki oth Fukasawa, Kimiaki oth Nagasue, Naofumi oth Nakamura, Teruhisa oth in Surgery today 1971 18(1988) vom: Mai, Seite 533-539 (DE-627)NLEJ188991352 (DE-600)1463169-6 1436-2813 nnns volume:18 year:1988 month:05 pages:533-539 extent:7 http://dx.doi.org/10.1007/BF02471487 GBV_USEFLAG_U ZDB-1-SOJ GBV_NL_ARTICLE AR 18 1988 5 533-539 7 |
allfieldsSound |
(DE-627)NLEJ20764215X DE-627 ger DE-627 rakwb eng The use of chitin as a new absorbable suture material—An experimental study 1988 7 nicht spezifiziert zzz rdacontent nicht spezifiziert z rdamedia nicht spezifiziert zu rdacarrier Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. Springer Online Journal Archives 1860-2002 Tachibana, Mitsuo oth Yaita, Akira oth Taniura, Hiroyuki oth Fukasawa, Kimiaki oth Nagasue, Naofumi oth Nakamura, Teruhisa oth in Surgery today 1971 18(1988) vom: Mai, Seite 533-539 (DE-627)NLEJ188991352 (DE-600)1463169-6 1436-2813 nnns volume:18 year:1988 month:05 pages:533-539 extent:7 http://dx.doi.org/10.1007/BF02471487 GBV_USEFLAG_U ZDB-1-SOJ GBV_NL_ARTICLE AR 18 1988 5 533-539 7 |
language |
English |
source |
in Surgery today 18(1988) vom: Mai, Seite 533-539 volume:18 year:1988 month:05 pages:533-539 extent:7 |
sourceStr |
in Surgery today 18(1988) vom: Mai, Seite 533-539 volume:18 year:1988 month:05 pages:533-539 extent:7 |
format_phy_str_mv |
Article |
institution |
findex.gbv.de |
isfreeaccess_bool |
false |
container_title |
Surgery today |
authorswithroles_txt_mv |
Tachibana, Mitsuo @@oth@@ Yaita, Akira @@oth@@ Taniura, Hiroyuki @@oth@@ Fukasawa, Kimiaki @@oth@@ Nagasue, Naofumi @@oth@@ Nakamura, Teruhisa @@oth@@ |
publishDateDaySort_date |
1988-05-01T00:00:00Z |
hierarchy_top_id |
NLEJ188991352 |
id |
NLEJ20764215X |
language_de |
englisch |
fullrecord |
<?xml version="1.0" encoding="UTF-8"?><collection xmlns="http://www.loc.gov/MARC21/slim"><record><leader>01000caa a22002652 4500</leader><controlfield tag="001">NLEJ20764215X</controlfield><controlfield tag="003">DE-627</controlfield><controlfield tag="005">20210706233604.0</controlfield><controlfield tag="007">cr uuu---uuuuu</controlfield><controlfield tag="008">070528s1988 xx |||||o 00| ||eng c</controlfield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-627)NLEJ20764215X</subfield></datafield><datafield tag="040" ind1=" " ind2=" "><subfield code="a">DE-627</subfield><subfield code="b">ger</subfield><subfield code="c">DE-627</subfield><subfield code="e">rakwb</subfield></datafield><datafield tag="041" ind1=" " ind2=" "><subfield code="a">eng</subfield></datafield><datafield tag="245" ind1="1" ind2="0"><subfield code="a">The use of chitin as a new absorbable suture material—An experimental study</subfield></datafield><datafield tag="264" ind1=" " ind2="1"><subfield code="c">1988</subfield></datafield><datafield tag="300" ind1=" " ind2=" "><subfield code="a">7</subfield></datafield><datafield tag="336" ind1=" " ind2=" "><subfield code="a">nicht spezifiziert</subfield><subfield code="b">zzz</subfield><subfield code="2">rdacontent</subfield></datafield><datafield tag="337" ind1=" " ind2=" "><subfield code="a">nicht spezifiziert</subfield><subfield code="b">z</subfield><subfield code="2">rdamedia</subfield></datafield><datafield tag="338" ind1=" " ind2=" "><subfield code="a">nicht spezifiziert</subfield><subfield code="b">zu</subfield><subfield code="2">rdacarrier</subfield></datafield><datafield tag="520" ind1=" " ind2=" "><subfield code="a">Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction.</subfield></datafield><datafield tag="533" ind1=" " ind2=" "><subfield code="f">Springer Online Journal Archives 1860-2002</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Tachibana, Mitsuo</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Yaita, Akira</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Taniura, Hiroyuki</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Fukasawa, Kimiaki</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Nagasue, Naofumi</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Nakamura, Teruhisa</subfield><subfield code="4">oth</subfield></datafield><datafield tag="773" ind1="0" ind2="8"><subfield code="i">in</subfield><subfield code="t">Surgery today</subfield><subfield code="d">1971</subfield><subfield code="g">18(1988) vom: Mai, Seite 533-539</subfield><subfield code="w">(DE-627)NLEJ188991352</subfield><subfield code="w">(DE-600)1463169-6</subfield><subfield code="x">1436-2813</subfield><subfield code="7">nnns</subfield></datafield><datafield tag="773" ind1="1" ind2="8"><subfield code="g">volume:18</subfield><subfield code="g">year:1988</subfield><subfield code="g">month:05</subfield><subfield code="g">pages:533-539</subfield><subfield code="g">extent:7</subfield></datafield><datafield tag="856" ind1="4" ind2="0"><subfield code="u">http://dx.doi.org/10.1007/BF02471487</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_USEFLAG_U</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">ZDB-1-SOJ</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_NL_ARTICLE</subfield></datafield><datafield tag="951" ind1=" " ind2=" "><subfield code="a">AR</subfield></datafield><datafield tag="952" ind1=" " ind2=" "><subfield code="d">18</subfield><subfield code="j">1988</subfield><subfield code="c">5</subfield><subfield code="h">533-539</subfield><subfield code="g">7</subfield></datafield></record></collection>
|
series2 |
Springer Online Journal Archives 1860-2002 |
ppnlink_with_tag_str_mv |
@@773@@(DE-627)NLEJ188991352 |
format |
electronic Article |
delete_txt_mv |
keep |
collection |
NL |
remote_str |
true |
illustrated |
Not Illustrated |
issn |
1436-2813 |
topic_title |
The use of chitin as a new absorbable suture material—An experimental study |
format_facet |
Elektronische Aufsätze Aufsätze Elektronische Ressource |
format_main_str_mv |
Text Zeitschrift/Artikel |
carriertype_str_mv |
zu |
author2_variant |
m t mt a y ay h t ht k f kf n n nn t n tn |
hierarchy_parent_title |
Surgery today |
hierarchy_parent_id |
NLEJ188991352 |
hierarchy_top_title |
Surgery today |
isfreeaccess_txt |
false |
familylinks_str_mv |
(DE-627)NLEJ188991352 (DE-600)1463169-6 |
title |
The use of chitin as a new absorbable suture material—An experimental study |
spellingShingle |
The use of chitin as a new absorbable suture material—An experimental study |
ctrlnum |
(DE-627)NLEJ20764215X |
title_full |
The use of chitin as a new absorbable suture material—An experimental study |
journal |
Surgery today |
journalStr |
Surgery today |
lang_code |
eng |
isOA_bool |
false |
recordtype |
marc |
publishDateSort |
1988 |
contenttype_str_mv |
zzz |
container_start_page |
533 |
container_volume |
18 |
physical |
7 |
format_se |
Elektronische Aufsätze |
title_sort |
the use of chitin as a new absorbable suture material—an experimental study |
title_auth |
The use of chitin as a new absorbable suture material—An experimental study |
abstract |
Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. |
abstractGer |
Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. |
abstract_unstemmed |
Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction. |
collection_details |
GBV_USEFLAG_U ZDB-1-SOJ GBV_NL_ARTICLE |
title_short |
The use of chitin as a new absorbable suture material—An experimental study |
url |
http://dx.doi.org/10.1007/BF02471487 |
remote_bool |
true |
author2 |
Tachibana, Mitsuo Yaita, Akira Taniura, Hiroyuki Fukasawa, Kimiaki Nagasue, Naofumi Nakamura, Teruhisa |
author2Str |
Tachibana, Mitsuo Yaita, Akira Taniura, Hiroyuki Fukasawa, Kimiaki Nagasue, Naofumi Nakamura, Teruhisa |
ppnlink |
NLEJ188991352 |
mediatype_str_mv |
z |
isOA_txt |
false |
hochschulschrift_bool |
false |
author2_role |
oth oth oth oth oth oth |
up_date |
2024-07-06T10:15:50.625Z |
_version_ |
1803824346562560000 |
fullrecord_marcxml |
<?xml version="1.0" encoding="UTF-8"?><collection xmlns="http://www.loc.gov/MARC21/slim"><record><leader>01000caa a22002652 4500</leader><controlfield tag="001">NLEJ20764215X</controlfield><controlfield tag="003">DE-627</controlfield><controlfield tag="005">20210706233604.0</controlfield><controlfield tag="007">cr uuu---uuuuu</controlfield><controlfield tag="008">070528s1988 xx |||||o 00| ||eng c</controlfield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-627)NLEJ20764215X</subfield></datafield><datafield tag="040" ind1=" " ind2=" "><subfield code="a">DE-627</subfield><subfield code="b">ger</subfield><subfield code="c">DE-627</subfield><subfield code="e">rakwb</subfield></datafield><datafield tag="041" ind1=" " ind2=" "><subfield code="a">eng</subfield></datafield><datafield tag="245" ind1="1" ind2="0"><subfield code="a">The use of chitin as a new absorbable suture material—An experimental study</subfield></datafield><datafield tag="264" ind1=" " ind2="1"><subfield code="c">1988</subfield></datafield><datafield tag="300" ind1=" " ind2=" "><subfield code="a">7</subfield></datafield><datafield tag="336" ind1=" " ind2=" "><subfield code="a">nicht spezifiziert</subfield><subfield code="b">zzz</subfield><subfield code="2">rdacontent</subfield></datafield><datafield tag="337" ind1=" " ind2=" "><subfield code="a">nicht spezifiziert</subfield><subfield code="b">z</subfield><subfield code="2">rdamedia</subfield></datafield><datafield tag="338" ind1=" " ind2=" "><subfield code="a">nicht spezifiziert</subfield><subfield code="b">zu</subfield><subfield code="2">rdacarrier</subfield></datafield><datafield tag="520" ind1=" " ind2=" "><subfield code="a">Abstract A comparative study of four absorbable suture materials, namely; poly-N-acetylglucosamine (Chitin), polyglycolic acid (PGA), plain catgut and chromic catgut, in terms of strength, elongation, tensile strength retention and tissue reaction, was undertaken. The straight pull strength of USP 3–0 size Chitin was over 2.6 kg, compared with PGA, which was over 3.4 kg and the catguts, which were over 2.0 kg. Chitin showed the lowest elongation among the four. The tensile strength retention (TSR) of Chitin in muscle was 45 per cent at 14 days and 7 per cent at 25 days, which was similar to that of PGA. The TSR of Chitin was maintained by 35 per cent in gastric juice, 97 per cent in bile and 100 per cent in pancreatic juice after immersion for 30 days. The corresponding values for PGA were 54 per cent, 0 per cent and 0 per cent, respectively, whereas both catguts had dissolved within 30 days. The tissue reaction of Chitin was similar to that of PGA, whereas the catguts caused more intense tissue reaction.</subfield></datafield><datafield tag="533" ind1=" " ind2=" "><subfield code="f">Springer Online Journal Archives 1860-2002</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Tachibana, Mitsuo</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Yaita, Akira</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Taniura, Hiroyuki</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Fukasawa, Kimiaki</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Nagasue, Naofumi</subfield><subfield code="4">oth</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Nakamura, Teruhisa</subfield><subfield code="4">oth</subfield></datafield><datafield tag="773" ind1="0" ind2="8"><subfield code="i">in</subfield><subfield code="t">Surgery today</subfield><subfield code="d">1971</subfield><subfield code="g">18(1988) vom: Mai, Seite 533-539</subfield><subfield code="w">(DE-627)NLEJ188991352</subfield><subfield code="w">(DE-600)1463169-6</subfield><subfield code="x">1436-2813</subfield><subfield code="7">nnns</subfield></datafield><datafield tag="773" ind1="1" ind2="8"><subfield code="g">volume:18</subfield><subfield code="g">year:1988</subfield><subfield code="g">month:05</subfield><subfield code="g">pages:533-539</subfield><subfield code="g">extent:7</subfield></datafield><datafield tag="856" ind1="4" ind2="0"><subfield code="u">http://dx.doi.org/10.1007/BF02471487</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_USEFLAG_U</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">ZDB-1-SOJ</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_NL_ARTICLE</subfield></datafield><datafield tag="951" ind1=" " ind2=" "><subfield code="a">AR</subfield></datafield><datafield tag="952" ind1=" " ind2=" "><subfield code="d">18</subfield><subfield code="j">1988</subfield><subfield code="c">5</subfield><subfield code="h">533-539</subfield><subfield code="g">7</subfield></datafield></record></collection>
|
score |
7.399349 |