Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures
Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-m...
Ausführliche Beschreibung
Autor*in: |
Friedl, O. [verfasserIn] |
---|
Format: |
Artikel |
---|---|
Sprache: |
Englisch |
Erschienen: |
2007 |
---|
Schlagwörter: |
---|
Anmerkung: |
© THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 |
---|
Übergeordnetes Werk: |
Enthalten in: Metallurgical and materials transactions / B - Springer US, 1994, 39(2007), 1 vom: 12. Dez., Seite 135-146 |
---|---|
Übergeordnetes Werk: |
volume:39 ; year:2007 ; number:1 ; day:12 ; month:12 ; pages:135-146 |
Links: |
---|
DOI / URN: |
10.1007/s11663-007-9098-2 |
---|
Katalog-ID: |
OLC2059768349 |
---|
LEADER | 01000caa a22002652 4500 | ||
---|---|---|---|
001 | OLC2059768349 | ||
003 | DE-627 | ||
005 | 20230516001558.0 | ||
007 | tu | ||
008 | 200820s2007 xx ||||| 00| ||eng c | ||
024 | 7 | |a 10.1007/s11663-007-9098-2 |2 doi | |
035 | |a (DE-627)OLC2059768349 | ||
035 | |a (DE-He213)s11663-007-9098-2-p | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
082 | 0 | 4 | |a 620 |a 660 |q VZ |
100 | 1 | |a Friedl, O. |e verfasserin |4 aut | |
245 | 1 | 0 | |a Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures |
264 | 1 | |c 2007 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ohne Hilfsmittel zu benutzen |b n |2 rdamedia | ||
338 | |a Band |b nc |2 rdacarrier | ||
500 | |a © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 | ||
520 | |a Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. | ||
650 | 4 | |a Hollow Sphere | |
650 | 4 | |a Fracture Process Zone | |
650 | 4 | |a Cell Wall Thickness | |
650 | 4 | |a Sphere Diameter | |
650 | 4 | |a Plateau Stress | |
700 | 1 | |a Motz, C. |4 aut | |
700 | 1 | |a Peterlik, H. |4 aut | |
700 | 1 | |a Puchegger, S. |4 aut | |
700 | 1 | |a Reger, N. |4 aut | |
700 | 1 | |a Pippan, R. |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Metallurgical and materials transactions / B |d Springer US, 1994 |g 39(2007), 1 vom: 12. Dez., Seite 135-146 |w (DE-627)182203832 |w (DE-600)1186125-3 |w (DE-576)038889196 |x 1073-5615 |7 nnns |
773 | 1 | 8 | |g volume:39 |g year:2007 |g number:1 |g day:12 |g month:12 |g pages:135-146 |
856 | 4 | 1 | |u https://doi.org/10.1007/s11663-007-9098-2 |z lizenzpflichtig |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a SYSFLAG_A | ||
912 | |a GBV_OLC | ||
912 | |a SSG-OLC-TEC | ||
912 | |a SSG-OLC-CHE | ||
912 | |a SSG-OLC-PHA | ||
912 | |a SSG-OLC-DE-84 | ||
912 | |a GBV_ILN_20 | ||
912 | |a GBV_ILN_30 | ||
912 | |a GBV_ILN_62 | ||
912 | |a GBV_ILN_70 | ||
912 | |a GBV_ILN_602 | ||
912 | |a GBV_ILN_2027 | ||
912 | |a GBV_ILN_4319 | ||
912 | |a GBV_ILN_4323 | ||
951 | |a AR | ||
952 | |d 39 |j 2007 |e 1 |b 12 |c 12 |h 135-146 |
author_variant |
o f of c m cm h p hp s p sp n r nr r p rp |
---|---|
matchkey_str |
article:10735615:2007----::xeietlnetgtoomcaiapoeteomtli |
hierarchy_sort_str |
2007 |
publishDate |
2007 |
allfields |
10.1007/s11663-007-9098-2 doi (DE-627)OLC2059768349 (DE-He213)s11663-007-9098-2-p DE-627 ger DE-627 rakwb eng 620 660 VZ Friedl, O. verfasserin aut Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures 2007 Text txt rdacontent ohne Hilfsmittel zu benutzen n rdamedia Band nc rdacarrier © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress Motz, C. aut Peterlik, H. aut Puchegger, S. aut Reger, N. aut Pippan, R. aut Enthalten in Metallurgical and materials transactions / B Springer US, 1994 39(2007), 1 vom: 12. Dez., Seite 135-146 (DE-627)182203832 (DE-600)1186125-3 (DE-576)038889196 1073-5615 nnns volume:39 year:2007 number:1 day:12 month:12 pages:135-146 https://doi.org/10.1007/s11663-007-9098-2 lizenzpflichtig Volltext GBV_USEFLAG_A SYSFLAG_A GBV_OLC SSG-OLC-TEC SSG-OLC-CHE SSG-OLC-PHA SSG-OLC-DE-84 GBV_ILN_20 GBV_ILN_30 GBV_ILN_62 GBV_ILN_70 GBV_ILN_602 GBV_ILN_2027 GBV_ILN_4319 GBV_ILN_4323 AR 39 2007 1 12 12 135-146 |
spelling |
10.1007/s11663-007-9098-2 doi (DE-627)OLC2059768349 (DE-He213)s11663-007-9098-2-p DE-627 ger DE-627 rakwb eng 620 660 VZ Friedl, O. verfasserin aut Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures 2007 Text txt rdacontent ohne Hilfsmittel zu benutzen n rdamedia Band nc rdacarrier © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress Motz, C. aut Peterlik, H. aut Puchegger, S. aut Reger, N. aut Pippan, R. aut Enthalten in Metallurgical and materials transactions / B Springer US, 1994 39(2007), 1 vom: 12. Dez., Seite 135-146 (DE-627)182203832 (DE-600)1186125-3 (DE-576)038889196 1073-5615 nnns volume:39 year:2007 number:1 day:12 month:12 pages:135-146 https://doi.org/10.1007/s11663-007-9098-2 lizenzpflichtig Volltext GBV_USEFLAG_A SYSFLAG_A GBV_OLC SSG-OLC-TEC SSG-OLC-CHE SSG-OLC-PHA SSG-OLC-DE-84 GBV_ILN_20 GBV_ILN_30 GBV_ILN_62 GBV_ILN_70 GBV_ILN_602 GBV_ILN_2027 GBV_ILN_4319 GBV_ILN_4323 AR 39 2007 1 12 12 135-146 |
allfields_unstemmed |
10.1007/s11663-007-9098-2 doi (DE-627)OLC2059768349 (DE-He213)s11663-007-9098-2-p DE-627 ger DE-627 rakwb eng 620 660 VZ Friedl, O. verfasserin aut Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures 2007 Text txt rdacontent ohne Hilfsmittel zu benutzen n rdamedia Band nc rdacarrier © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress Motz, C. aut Peterlik, H. aut Puchegger, S. aut Reger, N. aut Pippan, R. aut Enthalten in Metallurgical and materials transactions / B Springer US, 1994 39(2007), 1 vom: 12. Dez., Seite 135-146 (DE-627)182203832 (DE-600)1186125-3 (DE-576)038889196 1073-5615 nnns volume:39 year:2007 number:1 day:12 month:12 pages:135-146 https://doi.org/10.1007/s11663-007-9098-2 lizenzpflichtig Volltext GBV_USEFLAG_A SYSFLAG_A GBV_OLC SSG-OLC-TEC SSG-OLC-CHE SSG-OLC-PHA SSG-OLC-DE-84 GBV_ILN_20 GBV_ILN_30 GBV_ILN_62 GBV_ILN_70 GBV_ILN_602 GBV_ILN_2027 GBV_ILN_4319 GBV_ILN_4323 AR 39 2007 1 12 12 135-146 |
allfieldsGer |
10.1007/s11663-007-9098-2 doi (DE-627)OLC2059768349 (DE-He213)s11663-007-9098-2-p DE-627 ger DE-627 rakwb eng 620 660 VZ Friedl, O. verfasserin aut Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures 2007 Text txt rdacontent ohne Hilfsmittel zu benutzen n rdamedia Band nc rdacarrier © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress Motz, C. aut Peterlik, H. aut Puchegger, S. aut Reger, N. aut Pippan, R. aut Enthalten in Metallurgical and materials transactions / B Springer US, 1994 39(2007), 1 vom: 12. Dez., Seite 135-146 (DE-627)182203832 (DE-600)1186125-3 (DE-576)038889196 1073-5615 nnns volume:39 year:2007 number:1 day:12 month:12 pages:135-146 https://doi.org/10.1007/s11663-007-9098-2 lizenzpflichtig Volltext GBV_USEFLAG_A SYSFLAG_A GBV_OLC SSG-OLC-TEC SSG-OLC-CHE SSG-OLC-PHA SSG-OLC-DE-84 GBV_ILN_20 GBV_ILN_30 GBV_ILN_62 GBV_ILN_70 GBV_ILN_602 GBV_ILN_2027 GBV_ILN_4319 GBV_ILN_4323 AR 39 2007 1 12 12 135-146 |
allfieldsSound |
10.1007/s11663-007-9098-2 doi (DE-627)OLC2059768349 (DE-He213)s11663-007-9098-2-p DE-627 ger DE-627 rakwb eng 620 660 VZ Friedl, O. verfasserin aut Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures 2007 Text txt rdacontent ohne Hilfsmittel zu benutzen n rdamedia Band nc rdacarrier © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress Motz, C. aut Peterlik, H. aut Puchegger, S. aut Reger, N. aut Pippan, R. aut Enthalten in Metallurgical and materials transactions / B Springer US, 1994 39(2007), 1 vom: 12. Dez., Seite 135-146 (DE-627)182203832 (DE-600)1186125-3 (DE-576)038889196 1073-5615 nnns volume:39 year:2007 number:1 day:12 month:12 pages:135-146 https://doi.org/10.1007/s11663-007-9098-2 lizenzpflichtig Volltext GBV_USEFLAG_A SYSFLAG_A GBV_OLC SSG-OLC-TEC SSG-OLC-CHE SSG-OLC-PHA SSG-OLC-DE-84 GBV_ILN_20 GBV_ILN_30 GBV_ILN_62 GBV_ILN_70 GBV_ILN_602 GBV_ILN_2027 GBV_ILN_4319 GBV_ILN_4323 AR 39 2007 1 12 12 135-146 |
language |
English |
source |
Enthalten in Metallurgical and materials transactions / B 39(2007), 1 vom: 12. Dez., Seite 135-146 volume:39 year:2007 number:1 day:12 month:12 pages:135-146 |
sourceStr |
Enthalten in Metallurgical and materials transactions / B 39(2007), 1 vom: 12. Dez., Seite 135-146 volume:39 year:2007 number:1 day:12 month:12 pages:135-146 |
format_phy_str_mv |
Article |
institution |
findex.gbv.de |
topic_facet |
Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress |
dewey-raw |
620 |
isfreeaccess_bool |
false |
container_title |
Metallurgical and materials transactions / B |
authorswithroles_txt_mv |
Friedl, O. @@aut@@ Motz, C. @@aut@@ Peterlik, H. @@aut@@ Puchegger, S. @@aut@@ Reger, N. @@aut@@ Pippan, R. @@aut@@ |
publishDateDaySort_date |
2007-12-12T00:00:00Z |
hierarchy_top_id |
182203832 |
dewey-sort |
3620 |
id |
OLC2059768349 |
language_de |
englisch |
fullrecord |
<?xml version="1.0" encoding="UTF-8"?><collection xmlns="http://www.loc.gov/MARC21/slim"><record><leader>01000caa a22002652 4500</leader><controlfield tag="001">OLC2059768349</controlfield><controlfield tag="003">DE-627</controlfield><controlfield tag="005">20230516001558.0</controlfield><controlfield tag="007">tu</controlfield><controlfield tag="008">200820s2007 xx ||||| 00| ||eng c</controlfield><datafield tag="024" ind1="7" ind2=" "><subfield code="a">10.1007/s11663-007-9098-2</subfield><subfield code="2">doi</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-627)OLC2059768349</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-He213)s11663-007-9098-2-p</subfield></datafield><datafield tag="040" ind1=" " ind2=" "><subfield code="a">DE-627</subfield><subfield code="b">ger</subfield><subfield code="c">DE-627</subfield><subfield code="e">rakwb</subfield></datafield><datafield tag="041" ind1=" " ind2=" "><subfield code="a">eng</subfield></datafield><datafield tag="082" ind1="0" ind2="4"><subfield code="a">620</subfield><subfield code="a">660</subfield><subfield code="q">VZ</subfield></datafield><datafield tag="100" ind1="1" ind2=" "><subfield code="a">Friedl, O.</subfield><subfield code="e">verfasserin</subfield><subfield code="4">aut</subfield></datafield><datafield tag="245" ind1="1" ind2="0"><subfield code="a">Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures</subfield></datafield><datafield tag="264" ind1=" " ind2="1"><subfield code="c">2007</subfield></datafield><datafield tag="336" ind1=" " ind2=" "><subfield code="a">Text</subfield><subfield code="b">txt</subfield><subfield code="2">rdacontent</subfield></datafield><datafield tag="337" ind1=" " ind2=" "><subfield code="a">ohne Hilfsmittel zu benutzen</subfield><subfield code="b">n</subfield><subfield code="2">rdamedia</subfield></datafield><datafield tag="338" ind1=" " ind2=" "><subfield code="a">Band</subfield><subfield code="b">nc</subfield><subfield code="2">rdacarrier</subfield></datafield><datafield tag="500" ind1=" " ind2=" "><subfield code="a">© THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007</subfield></datafield><datafield tag="520" ind1=" " ind2=" "><subfield code="a">Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed.</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Hollow Sphere</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Fracture Process Zone</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Cell Wall Thickness</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Sphere Diameter</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Plateau Stress</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Motz, C.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Peterlik, H.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Puchegger, S.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Reger, N.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Pippan, R.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="773" ind1="0" ind2="8"><subfield code="i">Enthalten in</subfield><subfield code="t">Metallurgical and materials transactions / B</subfield><subfield code="d">Springer US, 1994</subfield><subfield code="g">39(2007), 1 vom: 12. Dez., Seite 135-146</subfield><subfield code="w">(DE-627)182203832</subfield><subfield code="w">(DE-600)1186125-3</subfield><subfield code="w">(DE-576)038889196</subfield><subfield code="x">1073-5615</subfield><subfield code="7">nnns</subfield></datafield><datafield tag="773" ind1="1" ind2="8"><subfield code="g">volume:39</subfield><subfield code="g">year:2007</subfield><subfield code="g">number:1</subfield><subfield code="g">day:12</subfield><subfield code="g">month:12</subfield><subfield code="g">pages:135-146</subfield></datafield><datafield tag="856" ind1="4" ind2="1"><subfield code="u">https://doi.org/10.1007/s11663-007-9098-2</subfield><subfield code="z">lizenzpflichtig</subfield><subfield code="3">Volltext</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_USEFLAG_A</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SYSFLAG_A</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_OLC</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-TEC</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-CHE</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-PHA</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-DE-84</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_20</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_30</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_62</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_70</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_602</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_2027</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_4319</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_4323</subfield></datafield><datafield tag="951" ind1=" " ind2=" "><subfield code="a">AR</subfield></datafield><datafield tag="952" ind1=" " ind2=" "><subfield code="d">39</subfield><subfield code="j">2007</subfield><subfield code="e">1</subfield><subfield code="b">12</subfield><subfield code="c">12</subfield><subfield code="h">135-146</subfield></datafield></record></collection>
|
author |
Friedl, O. |
spellingShingle |
Friedl, O. ddc 620 misc Hollow Sphere misc Fracture Process Zone misc Cell Wall Thickness misc Sphere Diameter misc Plateau Stress Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures |
authorStr |
Friedl, O. |
ppnlink_with_tag_str_mv |
@@773@@(DE-627)182203832 |
format |
Article |
dewey-ones |
620 - Engineering & allied operations 660 - Chemical engineering |
delete_txt_mv |
keep |
author_role |
aut aut aut aut aut aut |
collection |
OLC |
remote_str |
false |
illustrated |
Not Illustrated |
issn |
1073-5615 |
topic_title |
620 660 VZ Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures Hollow Sphere Fracture Process Zone Cell Wall Thickness Sphere Diameter Plateau Stress |
topic |
ddc 620 misc Hollow Sphere misc Fracture Process Zone misc Cell Wall Thickness misc Sphere Diameter misc Plateau Stress |
topic_unstemmed |
ddc 620 misc Hollow Sphere misc Fracture Process Zone misc Cell Wall Thickness misc Sphere Diameter misc Plateau Stress |
topic_browse |
ddc 620 misc Hollow Sphere misc Fracture Process Zone misc Cell Wall Thickness misc Sphere Diameter misc Plateau Stress |
format_facet |
Aufsätze Gedruckte Aufsätze |
format_main_str_mv |
Text Zeitschrift/Artikel |
carriertype_str_mv |
nc |
hierarchy_parent_title |
Metallurgical and materials transactions / B |
hierarchy_parent_id |
182203832 |
dewey-tens |
620 - Engineering 660 - Chemical engineering |
hierarchy_top_title |
Metallurgical and materials transactions / B |
isfreeaccess_txt |
false |
familylinks_str_mv |
(DE-627)182203832 (DE-600)1186125-3 (DE-576)038889196 |
title |
Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures |
ctrlnum |
(DE-627)OLC2059768349 (DE-He213)s11663-007-9098-2-p |
title_full |
Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures |
author_sort |
Friedl, O. |
journal |
Metallurgical and materials transactions / B |
journalStr |
Metallurgical and materials transactions / B |
lang_code |
eng |
isOA_bool |
false |
dewey-hundreds |
600 - Technology |
recordtype |
marc |
publishDateSort |
2007 |
contenttype_str_mv |
txt |
container_start_page |
135 |
author_browse |
Friedl, O. Motz, C. Peterlik, H. Puchegger, S. Reger, N. Pippan, R. |
container_volume |
39 |
class |
620 660 VZ |
format_se |
Aufsätze |
author-letter |
Friedl, O. |
doi_str_mv |
10.1007/s11663-007-9098-2 |
dewey-full |
620 660 |
title_sort |
experimental investigation of mechanical properties of metallic hollow sphere structures |
title_auth |
Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures |
abstract |
Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 |
abstractGer |
Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 |
abstract_unstemmed |
Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed. © THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007 |
collection_details |
GBV_USEFLAG_A SYSFLAG_A GBV_OLC SSG-OLC-TEC SSG-OLC-CHE SSG-OLC-PHA SSG-OLC-DE-84 GBV_ILN_20 GBV_ILN_30 GBV_ILN_62 GBV_ILN_70 GBV_ILN_602 GBV_ILN_2027 GBV_ILN_4319 GBV_ILN_4323 |
container_issue |
1 |
title_short |
Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures |
url |
https://doi.org/10.1007/s11663-007-9098-2 |
remote_bool |
false |
author2 |
Motz, C. Peterlik, H. Puchegger, S. Reger, N. Pippan, R. |
author2Str |
Motz, C. Peterlik, H. Puchegger, S. Reger, N. Pippan, R. |
ppnlink |
182203832 |
mediatype_str_mv |
n |
isOA_txt |
false |
hochschulschrift_bool |
false |
doi_str |
10.1007/s11663-007-9098-2 |
up_date |
2024-07-03T23:19:23.328Z |
_version_ |
1803601852058566656 |
fullrecord_marcxml |
<?xml version="1.0" encoding="UTF-8"?><collection xmlns="http://www.loc.gov/MARC21/slim"><record><leader>01000caa a22002652 4500</leader><controlfield tag="001">OLC2059768349</controlfield><controlfield tag="003">DE-627</controlfield><controlfield tag="005">20230516001558.0</controlfield><controlfield tag="007">tu</controlfield><controlfield tag="008">200820s2007 xx ||||| 00| ||eng c</controlfield><datafield tag="024" ind1="7" ind2=" "><subfield code="a">10.1007/s11663-007-9098-2</subfield><subfield code="2">doi</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-627)OLC2059768349</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-He213)s11663-007-9098-2-p</subfield></datafield><datafield tag="040" ind1=" " ind2=" "><subfield code="a">DE-627</subfield><subfield code="b">ger</subfield><subfield code="c">DE-627</subfield><subfield code="e">rakwb</subfield></datafield><datafield tag="041" ind1=" " ind2=" "><subfield code="a">eng</subfield></datafield><datafield tag="082" ind1="0" ind2="4"><subfield code="a">620</subfield><subfield code="a">660</subfield><subfield code="q">VZ</subfield></datafield><datafield tag="100" ind1="1" ind2=" "><subfield code="a">Friedl, O.</subfield><subfield code="e">verfasserin</subfield><subfield code="4">aut</subfield></datafield><datafield tag="245" ind1="1" ind2="0"><subfield code="a">Experimental Investigation of Mechanical Properties of Metallic Hollow Sphere Structures</subfield></datafield><datafield tag="264" ind1=" " ind2="1"><subfield code="c">2007</subfield></datafield><datafield tag="336" ind1=" " ind2=" "><subfield code="a">Text</subfield><subfield code="b">txt</subfield><subfield code="2">rdacontent</subfield></datafield><datafield tag="337" ind1=" " ind2=" "><subfield code="a">ohne Hilfsmittel zu benutzen</subfield><subfield code="b">n</subfield><subfield code="2">rdamedia</subfield></datafield><datafield tag="338" ind1=" " ind2=" "><subfield code="a">Band</subfield><subfield code="b">nc</subfield><subfield code="2">rdacarrier</subfield></datafield><datafield tag="500" ind1=" " ind2=" "><subfield code="a">© THE MINERALS, METALS & MATERIALS SOCIETY and ASM INTERNATIONAL 2007</subfield></datafield><datafield tag="520" ind1=" " ind2=" "><subfield code="a">Abstract Metallic foam was fabricated from 316L stainless steel spheres, where the bonding of the spheres was achieved by a sintering process. The mechanical behavior of a low-density material (0.3 g/$ cm^{3} $) with 2- and 4-mm sphere diameter and a high-density material (0.6 g/$ cm^{3} $) with 4-mm sphere diameter was investigated in compression and tension. The cell wall material of this hollow sphere structure (HSS) had different morphologies: dense and porous sintered walls were investigated. The cell wall morphology affects the Young’s modulus (stiffness) and the ductility of the HSS material. Defects, such as the cell wall porosity, lower the ductility of the material. Besides the quasi-static measurements, the HSS material was tested with a resonance frequency method (dynamic measurement), to obtain detailed information on the stiffness at different temperatures up to 700 °C. In-situ compression and tension tests were carried out to understand the deformation mechanisms on the scale of the single hollow spheres. The failure mechanisms in the vicinity of the sintering neck of the spheres was investigated. A doubling of the density leads to an increase of the plateau stress and the ultimate tensile stress of the material, whereas the ductility (strain to fracture) depended mainly on the cell wall morphology. Due to the mainly tensile loading of the cell walls in the vicinity of the sinter neck, the ultimate tensile strength doubled for the high-density HSS, in good agreement with theoretical considerations. In compression, the gain in the plateau stress was not as distinctive compared with the theoretical considerations assuming a bending dominated deformation. The influence of structural parameters, such as cell wall morphology, cell wall thickness, and sphere diameter, on the mechanical behavior is discussed.</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Hollow Sphere</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Fracture Process Zone</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Cell Wall Thickness</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Sphere Diameter</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Plateau Stress</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Motz, C.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Peterlik, H.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Puchegger, S.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Reger, N.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Pippan, R.</subfield><subfield code="4">aut</subfield></datafield><datafield tag="773" ind1="0" ind2="8"><subfield code="i">Enthalten in</subfield><subfield code="t">Metallurgical and materials transactions / B</subfield><subfield code="d">Springer US, 1994</subfield><subfield code="g">39(2007), 1 vom: 12. Dez., Seite 135-146</subfield><subfield code="w">(DE-627)182203832</subfield><subfield code="w">(DE-600)1186125-3</subfield><subfield code="w">(DE-576)038889196</subfield><subfield code="x">1073-5615</subfield><subfield code="7">nnns</subfield></datafield><datafield tag="773" ind1="1" ind2="8"><subfield code="g">volume:39</subfield><subfield code="g">year:2007</subfield><subfield code="g">number:1</subfield><subfield code="g">day:12</subfield><subfield code="g">month:12</subfield><subfield code="g">pages:135-146</subfield></datafield><datafield tag="856" ind1="4" ind2="1"><subfield code="u">https://doi.org/10.1007/s11663-007-9098-2</subfield><subfield code="z">lizenzpflichtig</subfield><subfield code="3">Volltext</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_USEFLAG_A</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SYSFLAG_A</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_OLC</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-TEC</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-CHE</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-PHA</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">SSG-OLC-DE-84</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_20</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_30</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_62</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_70</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_602</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_2027</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_4319</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">GBV_ILN_4323</subfield></datafield><datafield tag="951" ind1=" " ind2=" "><subfield code="a">AR</subfield></datafield><datafield tag="952" ind1=" " ind2=" "><subfield code="d">39</subfield><subfield code="j">2007</subfield><subfield code="e">1</subfield><subfield code="b">12</subfield><subfield code="c">12</subfield><subfield code="h">135-146</subfield></datafield></record></collection>
|
score |
7.398694 |